产品名称 | 焊接 工艺 |
硬度 HRC |
焊层合金名义成分 wt% | 特点及应用 | ||||||||||
C | Mn | Si | Cr | Ni | Mo | W | V | Nb | Fe | 其他 | ||||
WELD 226 | S | 20 | 0.1 | 1.0 | 0.5 | 1.0 | 0.8 | 0.5 | Bal | 良好的抗裂性,用于各种冶金轧辊打底层堆焊或恢复尺寸堆焊 | ||||
WELD 230 | S | 30 | 0.15 | 2.5 | 1.0 | 1.5 | Bal | |||||||
WELD 233 | S | 32 | 0.15 | 1.5 | 0.5 | 2.5 | 0.4 | Bal | 适中的硬度兼有良好的抗裂性,具备一定的抗金属间磨损性能,用于如输送辊道、天车轮、辊轴等的堆焊 | |||||
WELD 235 | S | 35 | 0.15 | 1.5 | 0.5 | 2.5 | 0.8 | 0.4 | Bal | |||||
WELD 240 | S | 40 | 0.2 | 1.5 | 0.5 | 3.0 | 0.5 | Bal | ||||||
WELD 243M | S | 44 | 0.2 | 1.5 | 0.5 | 5.0 | 1.2 | 1.5 | 0.25 | Bal | 兼有良好的机械强度和韧性,用于大型热轧支承辊的堆焊修复 | |||
WELD 245 | S | 45 | 0.15 | 2.0 | 0.5 | 5.0 | 3.5 | 3.5 | 0.25 | Bal | ||||
WELD 249S | S | 52 | 0.3 | 1.5 | 0.5 | 5.5 | 0.7 | 3.0 | 1.0 | 0.2 | Bal | 耐金属间磨损、抗冲击、抗冷热疲劳,可用于热轧工作辊的堆焊;兼有良好的抗粘钢性能,也可用于夹送辊、助卷辊、校直辊等堆焊 | ||
WELD 251 | S | 52 | 0.3 | 1.5 | 0.5 | 5.8 | 1.2 | 1.5 | 0.8 | Bal | ||||
WELD 251M | S | 54 | 0.35 | 1.5 | 0.5 | 5.8 | 1.2 | 1.6 | 0.8 | Bal | ||||
WELD 251Nb | S | 53 | 0.5 | 1.5 | 0.5 | 5.5 | 3.0 | 3.0 | Bal | 耐金属间磨损、良好的抗粘钢性能,用于夹送辊、助卷辊等堆焊 | ||||
WELD 254M | S | 54 | 0.35 | 1.5 | 0.5 | 6.0 | 0.8 | 2.0 | 3.5 | 0.25 | Bal | 耐金属间磨损、良好的抗粘钢性能,用于夹送辊、助卷辊等堆焊 | ||
WELD 255Nb | S | 57 | 0.7 | 1.5 | 0.5 | 5.0 | 3.0 | 3.0 | Bal | 优异的耐高温金属磨损性能,用于型钢开坯辊的耐磨堆焊 | ||||
WELD 258 | S | 58 | 0.5 | 1.5 | 0.5 | 6.5 | 2.0 | 3.0 | 0.7 | Bal | 耐金属间磨损、耐高温、抗冷热疲劳,用于助卷、夹送、矫直辊等堆焊 | |||
WELD 258W | S | 58 | 0.5 | 1.5 | 0.5 | 5.0 | 1.2 | 8.5 | 0.3 | Bal | 良好的抗金属间磨损性能 | |||
WELD 285 | S | 58 | 0.7 | 0.6 | 0.7 | 6.5 | 0.2 | 2.8 | 4.8 | 0.8 | 3.5 | Bal | Co2.8 | 优异的高温强度,用于高温条件下的抗金属间磨损 |
备注:S—埋弧焊,O—自保护焊,G—气保护焊,T—氩弧焊。