产品名称 | 焊接 工艺 |
硬度 HRC |
焊层合金名义成分 wt% | 特点及应用 | ||||||||||
C | Mn | Si | Cr | Ni | Mo | W | V | Nb | Fe | 其他 | ||||
WELD 410 | S | 38 | 0.1 | 1.5 | 0.5 | 13 | Bal | 用于耐高温腐蚀、抗金属间磨损工况的轧辊堆焊 | ||||||
WELD 415 | S | 52 | 0.4 | 1.5 | 0.5 | 16 | 0.6 | Bal | 用于耐高温腐蚀、抗金属间磨损工况的轧辊堆焊,2-3层即可达到Cr12 | |||||
WELD 417 | S | 40 | 0.05 | 1.5 | 0.5 | 17 | 4.0 | 0.3 | Bal | Cu4.0 | 630型合金,用于连铸辊等耐高温腐蚀、抗金属磨损工况的堆焊 | |||
WELD 420 | S | 45 | 0.2 | 1.5 | 0.5 | 13 | Bal | 耐金属间磨损、耐高温腐蚀、抗冷热疲劳,用于各种冶金轧辊堆焊 | ||||||
WELD 422 | S | 50 | 0.25 | 1.5 | 0.5 | 13.5 | 0.8 | 0.5 | 0.15 | Bal | 耐金属间磨损、耐高温腐蚀、抗冷热疲劳,用于热轧开坯辊堆焊 | |||
WELD 423M | S | 47 | 0.12 | 1.5 | 0.5 | 13 | 2.5 | 1.2 | 0.2 | 0.2 | Bal | 耐冷热疲劳、耐高温腐蚀,用于连铸辊、有色热轧辊等堆焊 | ||
WELD 423Co | S | 46 | 0.12 | 1.5 | 0.5 | 13.5 | 0.6 | 2.6 | 0.2 | 0.2 | Bal | Co13 | 耐高温腐蚀、抗冷热疲劳,用于高温工况下的热轧工作辊堆焊 | |
WELD 424MH | S | 50 | 0.25 | 1.5 | 0.5 | 14 | 1.4 | 1.1 | Bal | 耐金属间磨损、耐高温腐蚀、抗冷热疲劳,用于热轧开坯辊堆焊 | ||||
WELD 425 | S | 40 | 0.05 | 1.0 | 0.5 | 13 | 4.0 | 1.1 | Bal | 耐冷热疲劳、抗裂性好,用于连铸辊等堆焊 | ||||
WELD 428 | S | 52 | 0.4 | 1.5 | 0.5 | 12.5 | 0.7 | 1.3 | 0.4 | Bal | 耐金属间磨损、耐高温腐蚀,用于热轧工作辊、夹送辊、助卷辊等堆焊 | |||
WELD 428H | S | 55 | 0.4 | 1.5 | 0.5 | 11 | 3.0 | 1.0 | 0.4 | Bal | 耐金属间磨损、耐高温腐蚀,用于热轧工作辊、夹送辊、助卷辊等堆焊 | |||
WELD 414N | S | 42 | 0.05 | 1.2 | 0.6 | 13 | 4.0 | 1.0 | Bal | N0.07 | 耐高温腐蚀、抗冷热疲劳,用于连铸辊等堆焊 | |||
WELD 414N-O | O | 43 | 0.05 | 1.2 | 0.6 | 13 | 4.0 | 0.6 | Bal | N0.1 | 耐高温腐蚀、抗冷热疲劳,用于连铸辊等堆焊 | |||
WELD 423N | S | 44 | 0.05 | 1.2 | 0.6 | 13 | 4.2 | 1.3 | 0.2 | 0.2 | Bal | N0.07 | 耐高温腐蚀、抗冷热疲劳,用于连铸辊等堆焊 | |
WELD 423N-O | O | 44 | 0.05 | 1.2 | 0.6 | 14 | 4.5 | 0.6 | 0.1 | 0.1 | Bal | N0.1 | 耐高温腐蚀、抗冷热疲劳,用于连铸辊等堆焊 | |
WELD 430 | S | 25 | 0.05 | 1.2 | 0.6 | 18 | Bal | 抗高温氧化、耐锈蚀,用于连铸辊打底焊或各类金属耐锈蚀防护堆焊 | ||||||
WELD 430-O | O | 30 | 0.05 | 1.2 | 0.6 | 18 | Bal | 抗高温氧化、耐锈蚀,用于连铸辊打底焊或各类金属耐锈蚀防护堆焊 |
备注:S—埋弧焊,O—自保护焊,G—气保护焊,T—氩弧焊。