Product | Weld Procedure | Hardness HRC | Typical All Weld Metal Analysis (%) | Properties and Applications | ||||||||||
C | Mn | Si | Cr | Ni | Mo | W | V | Nb | Fe | Oth. | ||||
WELD 100PHT-O | O | 62 | 5.0 | 1.2 | 1.2 | 22 | Bal | B+ | High content of Cr-Carbides alloy in austenitic matrix, with good resistance to abrasion and low to medium impact. | |||||
WELD 100HC-O | O | 65 | 5.2 | 0.8 | 0.7 | 30 | Bal | 1.0 | Rich Cr-Carbides alloy in austenitic matrix, with excellent resistance to abrasion and low to medium impact. | |||||
WELD 100M2-O | O | 61 | 5.0 | 1.0 | 1.2 | 29 | Bal | Highly Cr-carbide alloyed, with excellent resistance to abrasion and medium impact. Can be applied as multi layers. Application: pump, mixer parts, conveyer screws, crusher rolls & grinding | ||||||
WELD 100Mo-O | O | 60 | 5.0 | 0.5 | 0.8 | 28 | 1.2 | Bal | ||||||
WELD 100Re-O | O | 62 | 5.0 | 1.0 | 1.2 | 28.5 | Bal | 0.5 | ||||||
WELD 100V-O | O | 64 | 5.2 | 0.6 | 1.0 | 27 | Mo+V+Nb+Re 4.5 | Rich Cr-carbide and complex carbides types, with excellent abrasion resistance. | ||||||
WELD 142H-O | O | 55 | 3.0 | 0.6 | 1.2 | 32 | 3.0 | 0.5 | bal | High content of C-Cr-Ni-Mo alloy with good abrasion resistance and a corrosion resistant matrix. Crack free weld is possible. | ||||
WELD 143-O | O | 62 | 5.2 | 0.6 | 1.0 | 22 | 6.5 | Bal | Strengthened by NbC carbides, poses better abrasion resistance than common Cr-C carbides alloy. | |||||
WELD 144-O | O | 62 | 5.0 | 1.0 | 1.0 | 25 | 5.5 | Bal | Strengthened by VC carbides, poses higher abrasion resistance than common Cr-C carbides alloy. | |||||
WELD 145-O | O | 65 | 5.3 | 0.3 | 0.8 | 20 | 4.8 | 1.8 | 1.0 | 6.0 | Bal | Highly alloyed with W/Mo/V/Nb, poses excellent abrasion resistance and high hardness at elevated temperature up to 800℃. | ||
WELD 145M2-O | O | 64 | 5.2 | 0.8 | 1.0 | 22 | 2.0 | 1.0 | 1.5 | 3.0 | Bal | Highly alloyed with W/Mo/V/Nb, poses excellent abrasion resistance and high hardness at elevated temperature up to 750℃. | ||
WELD 147-O | O | 65 | 6.0 | 1.0 | 1.0 | 37 | 0.8 | Bal | 0.8 | Very high C-Cr alloyed deposit, excellent resistance to extreme abrasion at elevated temperature. | ||||
WELD 150-O | O | 57 | 1.8 | 1.0 | 0.5 | 7.0 | 1.4 | Bal | Ti 5 | A high amount of titanium carbides in martensitic matrix, features good abrasion and impact resistance. | ||||
WELD 160-O | O | 58 | 3.5 | 0.6 | 1.0 | 32 | 0.5 | Bal | A highly C-Cr-Mo alloyed deposit for heavy mineral wear and minor corrosion, can be subjected to moderate impact stress. | |||||
WELD 164-O | O | 64 | 4.5 | 1.2 | 1.0 | 25 | 0.8 | 0.8 | Bal | B+ | Highly C-Cr-V-W alloyed, Resistant to heavy mineral at elevated temperature. Best results by welding in 1-2 layers. | |||
WELD 164M-O | O | 64 | 4.5 | 1.2 | 1.0 | 25 | 1.6 | Bal | B+ | Highly C-Cr-Mo alloyed, Resistant to heavy mineral at elevated temperature. Best results by welding in 1-2 layers. |
Notes:S—Sub-arc weld,O—Self-shielding weld,G—Gas shielding weld ,T—TIG weld